Xinghua reflective hot paste operation guide and precautions

Xinghua Reflective Hot Sticker has a variety of models to choose from according to the different needs of customers. For example, the color and reflectance can be divided into high heat paste and bright silver heat paste.

At the same time, in order to meet the needs of hot stamping, the company has special hot stamping for mapping, bright silver hot stamping with thickened PET film and bright silver hot stamping with adhesive film on the back for easy fixation.

For flame retardant, industrial washed or elastic fabrics, the company also has corresponding flame retardant hot stickers, industrial washable hot stickers and elastic hot stickers.

Operation guide:

Xinghua Reflective Hot Paste Hot Condition
machine Product number
Flat Pressing Machine Roller pressing machine
Temperature (℃) Pressing time (seconds) Pressure (kg / cm²) Temperature (℃) Roller speed (m / min) Pressure (kg / cm²)
CS 4002
Hot paste
140-160 8-20 > 0.5 120-140 4-8 > 2
CS 4002-T
Special hot stickers for lettering
140-160 8-20 > 0.5 120-140 4-8 > 2
CS 4003
Bright silver hot paste
140-160 8-20 > 0.5 120-140 4-8 > 2
CS-4003E
Bright silver elastic hot paste
150-170 10-20 > 0.5 130-150 4-8 > 2
CS-4003FR
Flame retardant hot paste
160-200 10-20 > 0.5 130-180 3-8 > 2
CS-4600
Industrial washable hot paste
160-200 10-20 > 0.5 130-180 3-8 > 2
CSR-4011
Hydrophobic Hot Sticker
100-160 12-60 > 0.5 120-140 4-8 > 2
CSR-4003D
Thick bright silver hot paste
145-165 8-20 > 0.5 125-145 4-8 > 2
CSR-4003-M
Bright silver hot sticker with adhesive film
145-165 8-20 > 0.5 125-145 4-8 > 2
CSR-4003E-M
Bright silver elastic hot sticker with adhesive film
155-175 10-20 > 0.5 135-155 4-8 > 2
CS-4008
Hot engraved strip
140-160 8-20 > 0.5 120-140 4-8 > 2
CS-4003-Z001-Y
Hot engraved strip
140-160 8-20 > 0.5 120-140 4-8 > 2

Precautions

1. The above hot stamping conditions are for reference only. Please make sure to test the fabric and hot stamping before the mass production to determine the best hot stamping conditions.

2. When there is a release pad film on the hot-melt adhesive surface of the hot paste, peel off the release film before applying it to the substrate during the trial;

3. If a flat-plate hot stamping method is used, a layer of cold cotton (gram weight 150-200g / m²) is covered on the hot-sealed product during the hot-pressing process to avoid the hot-heated hot stamping and the substrate caused by the instant high temperature. There are air bubbles in between.

4. Under the premise of ensuring fastness, the hot temperature cannot be too high, and the pressing time cannot be too long, so as not to deform the PE composite film if it is heated for too long, which will affect the appearance;

5. For higher temperatures, use the two-step method. First use the recommended temperature for about 2-3 seconds to fix the hot patch, remove the transparent PET film, and then use higher temperature for about 8-10 seconds.

6. After hot ironing, it is necessary to cool to the natural room temperature before tearing the protective film. When tearing the PE composite film as far as possible at 180 °, it needs to be removed at one time. It is not recommended to stop in the middle to avoid stopping marks and affecting the appearance;

7. Maintenance guide: It is recommended to use neutral detergent for hand washing. It is forbidden to pre-soak. It can be washed in hot water (40 ℃). It is forbidden to wash with bleach, strong acid and strong alkali.